Chemical composition % of steel X10CrNi18-8 (1.4310): EN 10088-2-2005 Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
1.4310, X10CrNi18-8, AISI 301 - description and application. Stainless, non-magnetic spring steel with high carbon content with good ductility delivered in the form of cold rolled tapes, sheets, drawn wires and drawn bars.
EN 1.4310 stainless steel is an austenitic stainless steel formulated for primary forming into wrought products. 1.4310 is the EN numeric designation for this material. X10CrNi18-8 is the EN chemical designation. It can have a moderately high tensile strength among wrought austenitic stainless steels.
X10CrNi18-8 can be supplied as steel plate/ sheet, round steel bar, steel tube/pipe, steel stripe, steel billet, steel ingot, steel wire rods. electroslag, forged ring/ block,etc. Join Supplier: [email protected]
This page cover the X10CrNi18-8 steel grades Mechanical Properties, Chemical Element, Cross Reference of Spain UNE X10CrNi18-8 Materials, Application Spain structural alloy steel,
Chemical composition % of the ladle analysis of grade X10CrNi18-8 (1.4310) Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
See the chemical composition and physical properties of X10CrNi18-8, find alternative materials, and connect with suppliers.
301 Stainless Steel 1.4310 is an austenitic spring steel. BSS supply 301 stainless in sheet and in coil, with next day dispatch. Grade 301 stainless steel is suitable for spring manufacture, scrapers, dental and medical applications, shims, printing applications and the food industry.
Contact Acerinox Headquarters. map icon C/ Santiago de Compostela n 100. 28035 Madrid. phone icon (+34) 91 398 51 00 / 91 398 51 02. fax icon (+34) 91 398 51 97. If you wish to contact directly with any of our delegations:
X10CrNi18-8 1.4310 C 0.05 0.15 Cr 16.00 19.00 Ni 6.00 9.50 Mo max. 0.80 N max. 0.11 1.4310 is essentially a leaner version of 1.4301, which as a result of its combination of high chromium and restricted nickel content, produces a metastable austenitic structure which will
In the atmosphere and acid, alkali, salt and other corrosive medium appears passivity, corrosion resistant and not rusty high chromium alloy (commonly 12% ~ 12%).Refers to stainless steel resistant to weak corrosive medium such as air, steam, water and acid, alkali, salt and other chemical etching medium corrosion of steel, also known as stainless acid-resisting steel.
types, by cold rolling. The 1.4310, X10CrNi18-8, is the most widely used stainless steel for the production of springs. It reaches very high mechanical strength through cold working. Its austenitic structure is rather unstable and its corrosion resistance is lower than, for example, that of the 1.4435, 316L, or of the 1.4301, X5CrNiMo 18-10.
It mainly introduce the chemical composition,mechanical properties, heat treatment, processing performance and performance standards about X10CrNi18-8.For various specification of steel production and processing to provide the standard production,we have the professional experience for X10CrNi18-8.We can also produce it according to the AISI, UNS, SAE, ASTM, DIN, JIS technical standard.
X10CrNi18-8 angle bars, X10CrNi18-8 flanges, Pipe Fitting, Steel Pipe, Heat Exchanger and Reducer, Gasket, Tee, Pipe Fitting, Tube Plate, have all specifications. With many yeas production experience, strict control X10CrNi18-8 chemical composition and X10CrNi18-8 mechanical properties.
The table below compares steel equivalent grades of materials from various international specifications. Note that materials compared are the nearest available grade and may have slight variations in actual chemistry.
The main production sales X10CrNi18-8 steel plate,X10CrNi18-8 sheet,X10CrNi18-8 coil,X10CrNi18-8 round bar,X10CrNi18-8 flat bar,X10CrNi18-8 tube/pipe products.
a 4310 werkstoffdatenblatt x10crni18-8 1.4310 nichtrostender austenitischer stahl chemische zusammensetzung (in massen-% nach din en 10088-3) c si mn p s cr ni mo n
din x10crni18-8, din x12crni177, anfor z11cn17-08, anfor z11cn18-08, anfor z12cn18-09, uni x12crni1707, jis sus301, jis sus301-csp, jis sus302, jis sus302fb, aisi 301, uns s30100, uns s30200 request 1
Stainless Steel 1.4310 is capable of high tensile strength following cold work.
Grade 1.4310 is an austenitic stainless steel. It is mainly being used in the spring production. Do you have any questions about the material or would you like to order?
Stainless steel 301 - 1.4310 is one of the many grades that thyssenkrupp Materials (UK) supply. We supply a vast range in various forms of stainless, aluminium and mild steel.
The selection of the appropriate stainless steel grade for each applic ation is the result of variou s considerations. In order to assis t the reader in this selection, Euro Inox makes the following tables of technical properties available: Chemical composition of stainless steels (flat products)
THINK!- MARYLAND METRICS - The One-Stop Source For Metric And British Sized Fasteners, Wrenches, Cutting, & Measuring Tools, Metal Shapes, Oil Seals, O-Rings, Mechanical Power Transmission Equipment,
Steel Grade Equivalent Table (EN, SAE/AISI, UNS, DIN, BS, UNI, JIS) The table below compares common grades of materials from various international specifications. Note that materials compared are the nearest available grade and may have slight variations in actual chemistry.
AISI 301 stainless steel is an austenitic stainless steel formulated for primary forming into wrought products. 301 is the AISI designation for this material.
Data Sheet Spring Steel Strip 1.4310 Page 1 of 3 Material Code X10CrNi18-8 (previous: X12CrNi17-7) Material Number 1.4310 (~ AISI 301) Quality according EN 10151 Tolerances according EN ISO 9445
Chemical composition % of steel X5CrNi18-10 (1.4301): EN 10088-2-2005 Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted.
X10CrNi18-8 is developed for enhanced creep resistance and for higher strength at temperatures above 1000F (537C). In most instances, the carbon content of the plate enables dual
Spring steel is a name given to a wide range of steels used in the manufacture of springs, prominently in automotive and industrial suspension applications. These steels are generally low-alloy manganese, medium-carbon steel or high-carbon steel with a very high yield strength.
Stainless steel grade 301 is usually supplied in the form of strips and wires, with a tensile strength of up to 1800 Mpa, to produce tempers ranging from 1/16 Hard to Full Hard. By subjecting grade 301 to controlled analysis it is capable of retaining sufficient ductility even in hard conditions , x10crni18 8
x10crni18-8 properties x10crni18-8 c1300 x10crni18-8 equivalent x10crni18 8 material